M2-jauhe metallin ruiskuvaluun
M2 steel is a high-carbon chromium tool steel commonly used for manufacturing cutting tools, molds, and other applications requiring high hardness and wear resistance. MIM (Metal Injection Molding) technology is a precision manufacturing process used to produce small, complex-shaped metal parts. It involves blending M2 steel powder with a plastic binder, injecting the mixture into a mold, heating the mixture to melt the plastic binder, and then solidifying the M2 steel powder to form the desired metal part. After heat treatment and mechanical processing, the final metal part is obtained.
Tuotetiedot
M2 steel is a high-carbon chromium tool steel commonly used for manufacturing cutting tools, molds, and other applications requiring high hardness and wear resistance. MIM (Metal Injection Molding) technology is a precision manufacturing process used to produce small, complex-shaped metal parts. It involves blending M2 steel powder with a plastic binder, injecting the mixture into a mold, heating the mixture to melt the plastic binder, and then solidifying the M2 steel powder to form the desired metal part. After heat treatment and mechanical processing, the final metal part is obtained.
Yleistä tietoa
| Lähtöpaikkakunta: | Changsha, Kiina |
| Merkki: | HLPOWDER |
| Tuotenumero: | M2 |
| Hiukkaskoko: | Halkaisija 50: 11 μm / Halkaisija 50: 12 μm |
| Certification: | ISO9001, ISO14001 |
| Minimitilausmäärä: | 20kg |
| Pakkaus tiedot: | Rautatynnyri |
| Toimitusaika: | 7-10 päivää |
Sovellukset
● Autoteollisuus
● Aerospace
● Lääketieteelliset laitteet
● Teolliset työkalut
● Consumer Electronics
tekniset tiedot
Powder Shape: Spherical
Kemiallinen koostumus:
| Metalliseos | Cr | Mo | V | Si | Mn | C | Fe |
| M2 | 4.75-5.50 | 1.10-1.50 | 0.80-1.20 | 0.80-1.20 | 0.20-0.50 | 0.32-0.45 | Bal |
Hiukkaskoko:
| Hiukkaskoko | Napautusherkkyys | Hiukkaskokojakauma | ||
| D10 | D50 | D90 | ||
| D50: 12 μm | > 4.8 | 3.5-5.5 | 11.5-13.5 | 22-26 |
| D50: 11 μm | > 4.8 | 3.0-4.5 | 10.0-12.0 | 19-23 |
Raaka-aineen suorituskykyparametri:
| Parametri | yksikkö | Arvo | alue | Testausmenetelmä |
| rahalaitosten | g/10 min | 1000 | 600-1400 | ISO 1133 (190 ℃, 21.6 kg) |
| Sintraustiheys | g / cm | 8.10 | 8.00-8.20 | ISO 3369 |
| SVT | - | 1.165 | 1.162-1.168 | - |
Sintrattuna tyypillinen suorituskyky:
| Tuottovahvuus | Vetolujuus | Venymä A10 (%) | Kovuus |
| 750 MPa | 1150 MPa | 1% | 50 HVC |
Paketti
MIM:lle: Jokainen PE-pakkaus + 20 kg:n tölkit tai 25 kg:n/50 kg:n rautatynnyri tai 250 kg:n rautatynnyri.