316L ruostumattomasta teräksestä valmistettu jauhe metallin ruiskuvaluun
316L stainless steel is a commonly used material for Metal Injection Molding (MIM). Metal Injection Molding is a process that combines metal powders with a binder to create complex-shaped parts using injection molding technology. The MIM process is particularly suitable for producing parts with complex internal structures, which are difficult or impossible to achieve with traditional forging or machining methods.
Tuotetiedot
316L stainless steel is a commonly used material for Metal Injection Molding (MIM). Metal Injection Molding is a process that combines metal powders with a binder to create complex-shaped parts using injection molding technology. The MIM process is particularly suitable for producing parts with complex internal structures, which are difficult or impossible to achieve with traditional forging or machining methods.
Yleistä tietoa
| Lähtöpaikkakunta: | Changsha, Kiina |
| Merkki: | HLPOWDER |
| Tuotenumero: | 316L |
| Hiukkaskoko: | Halkaisija 50: 11 μm / Halkaisija 50: 12 μm |
| Certification: | ISO9001, ISO14001 |
| Minimitilausmäärä: | 20kg |
| Pakkaus tiedot: | Rautatynnyri |
| Toimitusaika: | 7-10 päivää |
Sovellukset
● Kulutuselektroniikka
● Yhteydenpito
● Tietotekniikka
● Biolääketieteen laitteet
● Auto
● Kelloteollisuus
● Ilmailuteollisuus
tekniset tiedot
Kemiallinen koostumus:
| Metalliseos | Cr | Ni | Mo | Si | Mn | C | Fe |
| 316L | 16.0-18.0 | 10.0-14.0 | 2.00-3.00 | ≤ 1.00 | ≤ 2.00 | ≤ 0.03 | Bal |
Hiukkaskoko:
| Hiukkaskoko | Napautusherkkyys | Hiukkaskokojakauma | ||
| D10 | D50 | D90 | ||
| D50: 12 μm | > 4.8 | 3.5-5.5 | 11.5-13.5 | 22-26 |
| D50: 11 μm | > 4.8 | 3.0-4.5 | 10.0-12.0 | 19-23 |
Raaka-aineen suorituskykyparametri:
| Parametri | yksikkö | Arvo | alue | Testausmenetelmä |
| rahalaitosten | g/10 min | 1000 | 600-1400 | ISO 1133 (190 ℃, 21.6 kg) |
| Sintraustiheys | g / cm | 7.90 | 7.85-7.95 | ISO 3369 |
| SVT | 1.165 | 1.162-1.168 |
Sintrattuna tyypillinen suorituskyky:
| Tuottovahvuus | Vetolujuus | Venymä A10 (%) | Kovuus |
| 170 MPa | 520 MPa | 55% | 120 HV10 |